100μm Silicone-Coated PET Film with Light Release Force, High Residual Adhesion, and Strong Dimensional Stability
Product Overview
When a release film needs to hold its shape under heat and tension, thickness matters. 0.1mm PET Release Film is a 100μm silicone-coated polyester film developed for heavy-gauge release applications. It combines light release force with high residual adhesion and strong dimensional stability, making it suitable for demanding lamination, molding, and protective film processes.
Technical Characteristics
The following values are representative measured data for the 100μm specification. They are not guaranteed values.
- Base film thickness: 100 μm
- Features: Light release
- 31B Release strength (ordinary temperature × 24 hours): 0.07 N/50mm
- 31B Release strength (70°C × 24 hours): 0.12 N/50mm
- Residual adhesion ratio: 95%
- Adhesion (resistance to abrasion by toluene): Pass
- Wettability (mold release surface): 30 mN/m or less
- Base film heat resistance: 150°C for 30 minutes
Key Properties
- Light and consistent release force before and after heat aging
- High residual adhesion ratio of 95%
- Strong dimensional stability from a 100μm base film
- Reliable handling for slitting, lamination, and sheet cutting
Applications
0.1mm PET Release Film is used as a mold release film, carrier film, and protective film in composite molding, adhesive lamination, electronics processing, and general industrial release applications. It is suitable for both roll-to-roll and sheet-based production, especially where a heavier gauge is preferred.
Why Choose Us
We supply 0.1mm PET Release Film with stable release performance, consistent thickness, and flexible converting support. Custom slitting and sheet cutting are available on request.
Contact us today for pricing, stock details, or a sample of 0.1mm PET Release Film.