38μm Silicone-Coated PET Film with Stable Release Force and 95% Residual Adhesion
Product Overview
In lamination and molding lines, even a small change in release force can affect yield. 0.036mm PET Release Film is a 38μm silicone-coated polyester film designed for light release applications that demand consistency. It maintains stable release performance at room temperature and after heat aging, while keeping residual adhesion high so the surface it protects stays clean and functional.
Technical Characteristics
The following values are representative measured data for the 38μm specification. They are not guaranteed values.
- Base film thickness: 38 μm
- Features: Light release
- 31B Release strength (ordinary temperature × 24 hours): 0.07 N/50mm
- 31B Release strength (70°C × 24 hours): 0.12 N/50mm
- Residual adhesion ratio: 95%
- Adhesion (resistance to abrasion by toluene): Pass
- Wettability (mold release surface): 30 mN/m or less
- Base film heat resistance: 150°C for 30 minutes
Key Properties
- Light and repeatable release force before and after heat exposure
- High residual adhesion ratio of 95%
- Uniform release surface wettability
- Good mechanical handling for lamination and converting
Applications
0.036mm PET Release Film is used as a mold release film, carrier film, and protective film in composite molding, adhesive lamination, electronics processing, and general industrial release applications. It is suitable for both roll-to-roll and sheet-based production.